IMPROVING THE TECHNOLOGY OF LIQUIDATION OF WEAR – RESISTANT WHITE CAST IRON

Authors

  • Saidmakhamadov Nosir PhD Candidate, Tashkent State Technical University, University Street 2, Tashkent, Uzbekistan
  • Turakhodjaev Nodir DSc Professor, Tashkent State Technical University, University Street 2, Tashkent, Uzbekistan
  • Abdullaev Kamol Docent, Namangan Engineering – Construction Institute, Islam Karimov Street 12, Namangan
  • Saidkhodjaeva Shokhista Docent, Tashkent State Technical University, University Street 2, Tashkent, Uzbekistan
  • Tadjiev Nuritdin Researcher, Tashkent State Technical University, University Street 2, Tashkent, Uzbekistan

DOI:

https://doi.org/10.17605/OSF.IO/6AQ29

Keywords:

casting, induction furnace, microstructure

Abstract

In this article, the optimal mode of liquefaction of wear – resistant white cast iron alloy in an induction furnace is developed. In addition, the chemical composition of the alloy for wear – resistant white cast iron without reducing the mechanical properties was developed, which is cheap and resource – saving from the economic point of view, and the microstructures of the alloy were examined using a scanning electron microscope.Also, depending on the amount of carbon and chromium in the alloy, the fluidity of the alloy was determined, and quality cast products were obtained.

Downloads

Published

2022-08-22

Issue

Section

Articles

How to Cite

Saidmakhamadov Nosir, Turakhodjaev Nodir, Abdullaev Kamol, Saidkhodjaeva Shokhista, & Tadjiev Nuritdin. (2022). IMPROVING THE TECHNOLOGY OF LIQUIDATION OF WEAR – RESISTANT WHITE CAST IRON. International Journal of Innovations in Engineering Research and Technology, 9(8), 10-16. https://doi.org/10.17605/OSF.IO/6AQ29